YAWATA H-650 (For Earth and Sand Abrasion)
Classification : DIN 8555 : E 6-UM-60
Approvals : -
Application : Surfacing of Crusher parts, dipper teeth, shovel teeth, etc.
prev
next
Property
Classification
Req. = Requirement
Typ. = Typical results
N.S. = Not Specified
C.L.1 = Combined Limit for Mn + Ni + Cr + Mo
Mechanical Properties
Recommended Size and Power Range
< AC, DC+ >
Recommendations for Use
YAWATA H-650 is a low hydrogen type electrode for surfacing worn parts of various machinery to be used without machining. Deposited metal of about 700 Vickers hardness and martensitic structure provides excellent resistance to earth and sand abrasion.
DIN 8555 : E 6-UM-60
Chemical Composition|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
Ni
|
C.L.1
|
|
|
Req.
|
>0.4
|
N.S.
|
N.S.
|
N.S.
|
N.S.
|
N.S.
|
N.S.
|
N.S.
|
>5.0
|
|
Typ.
|
0.56
|
0.54
|
0.40
|
0.009
|
0.011
|
7.88
|
0.39
|
0.08
|
8.75
|
Typ. = Typical results
N.S. = Not Specified
C.L.1 = Combined Limit for Mn + Ni + Cr + Mo
|
Vicker(Hv)
|
Rockwell C (HRC)
|
Shore
|
Heat treatment
|
|
700
|
60
|
81
|
As welded; preheat, interpass 150๐C
|
| Diameter /Length (mm) |
3.2/350 | 4.0/400 | 5.0/450 | |
| Welding position | Current (A) | |||
| F, V | 90-130 | 140-180 | 160-240 | |
< AC, DC+ >
1. Use dry electrodes only. Damp electrodes should be re-dried at 300～350℃ for 60 minutes before use.
2. Preheating at more than 150℃
3. A buffer layer with low hydrogen electrode is required to surface hardening metal or to deposit multiple layer.
2. Preheating at more than 150℃
3. A buffer layer with low hydrogen electrode is required to surface hardening metal or to deposit multiple layer.
Related industries
Mining & Sugar